Bond Strength of Repaired Acrylic Denture Teeth Using Visible Light Cure Composite Resin
Saja Ali
Muhsin
Background:
Although bonding to denture teeth after surface treatment with chemical agents is desirable, there is little information on the use of Visible Light Cure composite resin (VLC) as bonding denture materials.
Objectives:
To determine the effect of various surface treatments on shear bond strength between Visible Light Cure composite resin and the acrylic denture teeth interface.
Methods:
Forty cylindrical sticks of acrylic resin with denture teeth mounted atop were prepared. Various treatments were implemented upon the acrylic resin teeth surfaces. The samples were divided into four groups (n = 10). Light-cured composite resin (LC) was applied over all treated and untreated surfaces of tested groups. The shear bond was tested using a universal tensile testing apparatus with the knife-edge of a 0.8mm shear tester. Data were statistically analyzed using one-way ANOVA performed at a confidence level of 95% and significant P-value of (P ≤ 0.05).
Results:
Analysis of variance (ANOVA) showed statistically significant difference (P < 0.05) between treated and untreated teeth surfaces. The treated surfaces exhibited various levels of bond strength depending on the type of treatment.
Conclusion:
Application of VLC bonding agent with prior treatment of methylmethacrylate (MMA) on the acrylic resin denture teeth resulted in maximum bond strength with composite resin.
01
31
2017
57
64
TODENTJ-11-57
1
10.2174/crossmark_policy
opendentistryjournal.com
benthamopen.com
true
Peer Reviewed
Single blind
Checked with iThenticate
2016-06-21
2016-12-29
2017-1-03
2017-01-31
https://creativecommons.org/licenses/by/4.0/legalcode
10.2174/1874210601711010057
1553506956
https://opendentistryjournal.com/VOLUME/11/PAGE/57/
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.pdf
-
https://opendentistryjournal.com/contents/volumes/V11/TODENTJ-11-57/TODENTJ-11-57.xml
J. Prosthet. Dent.
Spratley M.H.
58
389
1987
10.1016/0022-3913(87)90065-5
Spratley MH.
An investigation of the adhesion of acrylic resin teeth to dentures.
J Prosthet Dent
1987;
58
(3)
: 389-92.
J. Prosthet. Dent.
Clancy J.M.
61
457
1989
10.1016/0022-3913(89)90014-0
Clancy JM, Boyer DB.
Comparative bond strengths of light-cured, heat-cured, and autopolymerizing denture resins to denture teeth.
J Prosthet Dent
1989;
61
(4)
: 457-62.
J. Prosthet. Dent.
Vergani C.E.
77
328
1997
10.1016/S0022-3913(97)70193-8
Vergani CE, Giampaolo ET, Cucci AL.
Composite occlusal surfaces for acrylic resin denture teeth.
J Prosthet Dent
1997;
77
(3)
: 328-31.
Int. Dent. J.
Yanikoglu D.N.
52
20
2002
10.1111/j.1875-595X.2002.tb00592.x
Yanikoglu DN, Duymus DZ, Bayindir DF.
Comparative bond strengths of autopolymerising denture resin and light cured composite resin to denture teeth.
Int Dent J
2002;
52
(1)
: 20-4.
J. Prosthet. Dent.
Kawara M.
66
566
1991
10.1016/0022-3913(91)90525-2
Kawara M, Carter JM, Ogle RE, Johnson RR.
Bonding of plastic teeth to denture base resins.
J Prosthet Dent
1991;
66
(4)
: 566-71.
J. Dent.
Cunningham J.L.
21
274
1993
10.1016/0300-5712(93)90106-Z
Cunningham JL.
Bond strength of denture teeth to acrylic bases.
J Dent
1993;
21
(5)
: 274-80.
J. Prosthet. Dent.
Stameisen A.E.
58
119
1987
10.1016/S0022-3913(87)80155-5
Stameisen AE, Ruffino A.
Replacement of lost or broken denture teeth with composites.
J Prosthet Dent
1987;
58
(1)
: 119-20.
Oper. Dent.
Turner C.W.
18
187
1993
Turner CW, Meiers JC.
Repair of an aged, contaminated indirect composite resin with a direct, visible-light-cured composite resin.
Oper Dent
1993;
18
(5)
: 187-94.
Oper. Dent.
Reis A.
26
287
2001
Reis A, Francci C, Loguercio AD, Carrilho MR, Rodriques Filho LE.
Re-attachment of anterior fractured teeth: fracture strength using different techniques.
Oper Dent
2001;
26
(3)
: 287-94.
Van Noort R.
Introduction to dental materials. 4th ed.
Mosby: Elsevier 2013.
J. N. J. Dent. Assoc.
Nicholas W.T.
58
41
1987
Nicholas WT.
Correction of acrylic denture tooth wear with light-cured composite resin.
J N J Dent Assoc
1987;
58
(1)
: 41-4.
J. Prosthet. Dent.
Weiner S.
57
381
1987
10.1016/0022-3913(87)90318-0
Weiner S, Krause AS, Nicholas W.
Esthetic modification of removable partial denture teeth with light-cured composites.
J Prosthet Dent
1987;
57
(3)
: 381-4.
Johnson T, Wood DJ.
Techniques in complete denture technology.
John Wiley & Sons 2012; pp.
51-3.
J. Dent. Res.
Pavarina A.C.
1071
1999
Pavarina AC, Souza J, Buso L.
Bond strength between composite resin and acrylic denture teeth. Effect of surface treatments.
J Dent Res
1999;
1071.
Int. J. Prosthodont.
Lagouvardos P.E.
16
499
2003
Lagouvardos PE, Polyzois GL.
Shear bond strength between composite resin and denture teeth: effect of tooth type and surface treatments.
Int J Prosthodont
2003;
16
(5)
: 499-504.
J. Prosthet. Dent.
Papazoglou E.
82
573
1999
10.1016/S0022-3913(99)70056-9
Papazoglou E, Vasilas AI.
Shear bond strengths for composite and autopolymerized acrylic resins bonded to acrylic resin denture teeth.
J Prosthet Dent
1999;
82
(5)
: 573-8.
Int. J. Prosthodont.
Vergani C.E.
13
383
2000
Vergani CE, Machado AL, Giampaolo ET, Pavarina AC.
Effect of surface treatments on the bond strength between composite resin and acrylic resin denture teeth.
Int J Prosthodont
2000;
13
(5)
: 383-6.
Dent. Mater.
Swift E.J.
8
362
1992
10.1016/0109-5641(92)90020-D
Swift EJ Jr, LeValley BD, Boyer DB.
Evaluation of new methods for composite repair.
Dent Mater
1992;
8
(6)
: 362-5.
J. Prosthet. Dent.
Caswell C.W.
55
701
1986
10.1016/0022-3913(86)90447-6
Caswell CW, Norling BK.
Comparative study of the bond strengths of three abrasion-resistant plastic denture teeth bonded to a cross-linked and a grafted, cross-linked denture base material.
J Prosthet Dent
1986;
55
(6)
: 701-8.
J. Indian Prosthodont. Soc.
Chatterjee N.
11
20
2011
10.1007/s13191-011-0053-1
Chatterjee N, Gupta TK, Banerjee A.
A study on effect of surface treatments on the shear bond strength between composite resin and acrylic resin denture teeth.
J Indian Prosthodont Soc
2011;
11
(1)
: 20-5.
J. Biomed. Mater. Res.
Suzuki S.
24
1091
1990
10.1002/jbm.820240811
Suzuki S, Sakoh M, Shiba A.
Adhesive bonding of denture base resins to plastic denture teeth.
J Biomed Mater Res
1990;
24
(8)
: 1091-103.
J. Prosthet. Dent.
Clancy J.M.
65
315
1991
10.1016/0022-3913(91)90182-V
Clancy JM, Hawkins LF, Keller JC, Boyer DB.
Bond strength and failure analysis of light-cured denture resins bonded to denture teeth.
J Prosthet Dent
1991;
65
(2)
: 315-24.
Int. J. Prosthodont.
Hayakawa I.
4
561
1991
Hayakawa I, Hirano S, Nagao M, Matsumoto T, Masuhara E.
Adhesion of a new light-polymerized denture base resin to resin teeth and denture base materials.
Int J Prosthodont
1991;
4
(6)
: 561-8.
J. Prosthet. Dent.
Geerts G.A.
70
406
1993
10.1016/0022-3913(93)90075-Y
Geerts GA, Jooste CH.
A comparison of the bond strengths of microwave- and water bath-cured denture material.
J Prosthet Dent
1993;
70
(5)
: 406-9.
Aust. Dent. J.
Chung R.W.
40
241
1995
10.1111/j.1834-7819.1995.tb04804.x
Chung RW, Clark RK, Darvell BW.
The bonding of cold-cured acrylic resin to acrylic denture teeth.
Aust Dent J
1995;
40
(4)
: 241-5.
Biomaterials
Lastumäki T.M.
23
4533
2002
10.1016/S0142-9612(02)00197-7
Lastumäki TM, Kallio TT, Vallittu PK.
The bond strength of light-curing composite resin to finally polymerized and aged glass fiber-reinforced composite substrate.
Biomaterials
2002;
23
(23)
: 4533-9.
J. Am. Dent. Assoc.
Rupp N.
83
601
1971
10.14219/jada.archive.1971.0355
Rupp N, Bowen R, Paffenbarger G.
Bonding cold-curing denture base acrylic resin to acrylic resin teeth.
J Am Dent Assoc
1971;
83
(3)
: 601-6.
J. Prosthet. Dent.
Shen C.
52
844
1984
10.1016/S0022-3913(84)80016-5
Shen C, Colaizzi FA, Birns B.
Strength of denture repairs as influenced by surface treatment.
J Prosthet Dent
1984;
52
(6)
: 844-8.
J. Prosthet. Dent.
Vallittu P.K.
78
194
1997
10.1016/S0022-3913(97)70125-2
Vallittu PK, Ruyter IE, Nat R.
The swelling phenomenon of acrylic resin polymer teeth at the interface with denture base polymers.
J Prosthet Dent
1997;
78
(2)
: 194-9.
Int. J. Prosthodont.
Guzman A.
8
179
1995
Guzman A, Moore BK.
Influence of surface treatment on bond strength between a heat-activated and a light-activated resin composite.
Int J Prosthodont
1995;
8
(2)
: 179-86.
Quintessence Int.
Thean H.P.
27
425
1996
Thean HP, Chew C-L, Goh KI.
Shear bond strength of denture teeth to base: a comparative study.
Quintessence Int
1996;
27
(6)
: 425-8.